SATA-GF-M13 flux is a synthetic anhydrous carnallite inorganic salt fused together by different proportion, which has multi-functions in one, such as refining, drossing, covering, degassing, etc. SATA-GF-M13 flux is excellent in removing non-metallic inclusions (oxides, carbides and borides) and alkali metals (Na, Li, Ca) from molten aluminum and aluminum alloys. An eutectic can be formed to make the melting point of fluxes lower than 480 ℃. There is none sodium content in SATA-GF-M13, so as to avoid the phenomenon of “sodium brittle”. SATA-GF-M13 flux is environment-friendly with less fume and dust, which conforms to Emission Standards of Environmental Protection Agency (USA).
Application of SATA-GF-M13
Suitable for 1xxx/5xxx/6xxx aluminum alloys
Used to remove non-metallic inclusions in molten aluminum
Compared with M11 and M12 , M13 is featured with excellent performance on removing alkali metals
By Injector with inert gas can improve degassing, reduce metal porosity, achieving high refining performance
Obtain dry and loose drosses
Advantage of SATA-GF-M13
Prevent furnaces, launders, in-line degassors and casting nozzles from piling sludge and slag
Less dust and fume, and low dosage
Reduce metal loss
Low melting point for rapid dispersion
Improve mechanical and casting properties of aluminum alloys, and improve their quality
Specification of SATA-GF-M13
Furnace temperature: 680-720℃
Dosage: 0.25-1.2kg/MT
Appearance: off-white granule
Grain size: 1-3mm/0.8-3.25mm/1-2.5mm
Shelf life: 12 months
Package of SATA-GF-M13
Packed in 5kg (PE), 25kg (PP), 1000kg bags or customized.
Stored in dry, well-ventilated place, and avoid direct sunlight.
September 18, 2019SATA-GF-M11General Description of SATA-GF-M11SATA-GF-M11 flux is a synthetic anhydrous carnallite inorganic salt fused together by different proportion, which has multi-functions in one, such as refin...view
September 28, 2018General introductionMagnesium plays a very important part in producing the required physical properties of many aluminium alloys, its presence in others is not required at all or must be held to a ver...view
September 18, 2019Mn TabletGeneral Description of Mn TabletMn Tablet is used to adjust the content of Mn in Aluminium Alloy; it is made by metal powder and pure aluminium in proportion.Density:3.8-4.1g/cm3Content: meta...view
October 13, 2021General Description of Granulated Fused Refining Flux for Aluminium Cable &wiresAluminium Cable &wires is a kind of 1xxx and 6xxx series alloy, requires the aluminium alloy with good electrica...view