Jinzhou Sata Fused Fluxes and New Materials Factory.
Flux Injection Machine
Flux Injection Machine
Flux Injection Machine

Description:

In order to ensure the uniformity of the alloy and improve the quality of molten aluminum, aluminum alloy foundry companies mostly use furnace refining processes; inert gas (nitrogen or argon) is used as a carrier to spray powder or granular refining fluxes in the furnace aluminum liquid for refining which can achieve degassing and slag removal of molten aluminum.
With many years of experience in aluminum processing, production and processing, developed injection equipment which is a simple structure, easy handling, timing and quantitative injection machine.and the amount of fluxes spraying can be adjusted according to the production process. The spraying is uniform and not easy to be blocked. It can effectively improve the internal crystallization of the alloy and reduce the impurities in the aluminum alloy casting products; make the refining process in the furnace fully achieve the effect of refining, degassing and slagging.

Advantage:

1. The unique feeding device brings the flux into the molten aluminum uniformly and continuously,flux can fully contact with the molten aluminum, which prolongs the refining time maximizesthe function of the flux, reduces the dosage of flux. 
2. The Siemens TTCS realizes that one button adjust the flux adding speed from 0-2500g/min.
3. It is suitable for various working modes of pure gas refining, gas + granule or gas + powder flux. (Button on 0 realize the pure gas refining.)
4. Rotary quantitative feeding to achieve uniform supply flow,pipeline is not blocked.
5. Stainless flux container is sealed structure. Durable rotating shaft,wear-resistant,no leakage gas and flux
6. The flux container capacity is 50-100kgs ,can be customized.

Technical Data

Dimension 120×53×117㎝
feeder Capacity 50kg
Voltage 220V
Motor Power 120W
Feeding Speed 0~2500g/min
Gas Flow Rate 20~40L/min
Gas Pressure 0~0.25MPa
N.W.of Machine 100㎏

See More
  • Master Alloy

    Master Alloy

    September 18, 2019Master AlloyDescription of Master AlloySATA-Master alloys melt at a lower temperature as compared to primary metals. Controlled addition makes it easier to produce the final alloy of consistent compos...view
  • SATA-GF-M13

    SATA-GF-M13

    September 18, 2019SATA-GF-M13General Description of SATA-GF-M13SATA-GF-M13 flux is a synthetic anhydrous carnallite inorganic salt fused together by different proportion, which has multi-functions in one, such as refin...view
  • 2# Flux

    2# Flux

    September 28, 2018General introduction1) It used as a washing and melt covering for crucible, ladle and other tools for smelting and casting mag and mag alloy with the features of good wetting ability with the molten m...view
  • Cu Tablet

    Cu Tablet

    September 18, 2019Cu TabletGeneral Description of Cu TabletCu Tablet is used to adjust the content of Cu in Aluminium Alloy; it is made by metal powder and pure aluminium in proportion. Density:3.8-4.1g/cm3Content: met...view
Leave a Message Email Us

we will contact you within 24 hours.