Practice has proved that the hydrogen is the main cause of the pores in the aluminium alloy, the pores not only reduce the actual cross-sectional area of the casting, but also the source of the crack, so it is important part that removing the hydrogen during the smelting process.
SATA-degassing flux is a kind of traditional high efficiency degassing flux for aluminium and its alloys, it used for removing hydrogen and oxides from the aluminium melting.

Application of Degassing Flux (SATA-PF-350)

Plunge suitable quantity flux to the bottom (100mm from the bottom is better) of the melt, evenly and slowly remove the lunch, make the flux fully react with aluminium molten, stand or stir the molten for 10-15 min, the hydrogen and oxide will be taken out of aluminium molten.

Advantage of Degassing Flux (SATA-PF-350)

  • Easy operation, There are two options. One is with hexachloroethane in tablet form.and another is in powder form without hexachloroethane
  • It has excellent performance in refining, degassing and drossing
  • It can enhance the quality of casting, hydrogen content of aluminium molten can reduce to ≤0.1ml/100gAl, the oxide inclusion(Al2O3) can reduce 20% min, the casting inclusion defect reduce 50%min

Specification of Degassing Flux (SATA-PF-350)

  • White mixed powder
  • It is suit for all series alloy except high magnesium alloy,
  • Dosage: recommended dosage: 3%-5% large melting furnace, 4%-6% for crucible furnace
  • Working Temperature: 710℃-780℃

Package of Degassing Flux (SATA-PF-350)

  • Packed in 5kg (PE), 25kg (PP), 1000kg bags or customized.
  • Stored in dry, well-ventilated place, and avoid direct sunlight, keep sealed before using.

NOTE: This flux has serious hygroscopicity, please use immediately after opening.
See More
  • CAF2

    CAF2

    September 28, 2018General Description of Fluorspar (CaF2)Purity: 40%-99% in the form of powder and lumpSize :Metallurgical grade fluorspar: 0-10mm 10-60mm 20-70mm 30-80mmPurity: 60%-99.5%Acid grade fluorspar: 200m...view
  • Fe Tablet

    Fe Tablet

    September 18, 2019Fe TabletGeneral Description of Fe TabletFe Tablet is used to adjust the content of Fe in Aluminium Alloy; it is made by metal powder and pure aluminium in proportion.Density:3.8-4.1g/cm3Content: meta...view
  • Slagging Fluxes For Steel

    Slagging Fluxes For Steel

    December 25, 2020Description & Application of Slagging Fluxes For SteelCompare with the Caf2,This kind of flux can reduce 40-60% of the dosage than Caf2. At the meanwhile reduce the emission of SIF4 and other harm...view
  • Magnesium Chloride Hexahydrate Powder

    Magnesium Chloride Hexahydrate Powder

    September 28, 2018General Introduction:Chemical formular: Mgcl2 6H2OPurity: 46.00%min.Appearance: pure white crystal powderCAS NO.:7791-18-6Chemically, magnesium chloride is represented as MgCl2. It is a naturally occu...view
Leave a Message Email Us

we will contact you within 24 hours.