M-series Flux
M-series Flux
General Introduction:
M series Flux do not contain various forms of Na, which is suitable for Mg>2% Al-Alloy, this flux can effective remove non-metallic inclusions, hydrogen, sodium, calcium and lithium from the al and al-alloy liquid, and avoid the sodium brittle. Enhance degassing when injectedflux with Argon or Nitrogen.

F-101
  • Applied range: 1xx&3xx&8xx series alloy
  • Usage temperature: 700-760℃
  • Main chemical composition: chlorine salt & other chemicals, Na free
  • Color: off-white or white

F-102
  • Applied Range: 1xx&5xx&6xx series alloy
  • Usage temperature: 680-720℃
  • Main chemical composition: chlorine salt & fluoride salt &other chemicals, Na free
  • Color: off-white

F-103
  • Applied Range: 1xx&5xx&6xx series alloy
  • Usage temperature: 680-720℃
  • Main chemical composition: chlorine salt & fluoride salt &other chemicals, Na free
  • Color: off-white

This kind of fused flux is mixed the dry raw material together, then these material fused or melted in a high temperature furnace, in this process, the toxic such as chlorine will be released, after fusing completed, the flux are cooled into a huge block, finally it will be crushed or ground into customized particle size.
Instruction: this kinds of flux has a high efficient

By means of flux injection Machine gives the highest refining efficiency.
Sodium levels less than 1ppm in high Mg-al alloys are attainable in the casting.

Advantage:
  • Eco‐friendly flux that reduce dust levels, meet the emission limits of most environmental regulatory agencies
  • Uniform size, reacts fully. Purify the melt improve melt quality.
  • Increases the extrusion speed and die life when extruding profiles
  • Reduces the number of breaks in continuous casting
  • Eliminates edge cracks when rolling high Mg aluminium alloys
  • Free of fluorides. Zero fluoride emissions.
  • Low melting point for rapid dispersion


STAT-M-F101

SATA-M-F102

SATA-M-F103

composition

Chlorine salt

Na Free

Chlorine salt & fluoride

Salt, Na free

Chlorine salt & fluoride

Salt, Na free


Applied range

Suitable for Mg>2% alloy

1xx&3xx&8xx series alloy

1xx&5xx&6xx series alloy

1xx&5xx&6xx series alloy

Usage temperature

700-760℃

680-720℃

680-720℃

Dosage

Injection dosage:0.15%-0.2%

Size

Granulated :1mm-3mm

Color

Off white or white

Off white

Off white

Feature

Refining and slagging in furnace ,Eco-friendly

Refining and slagging in furnace ,Eco-friendly

Refining and slagging in furnace ,Eco-friendly


Similar Products
  • AlSr Modifiers

    AlSr Modifiers

    September 28, 2018General introduction For foundry alloys an important master alloy is the Aluminium-Strontium or AlSr "Modifier". It usually added into molten Al-Si alloys. which improves the mechanical properties in...view
  • Recovery Flux

    Recovery Flux

    September 28, 2018Application: Mainly used for primary aluminium ,aluminium alloy and secondary aluminium. It can be used for remove the floating dross on the surface of the molten aluminium, and can absorb slag near t...view
  • Sodium-Free Refining Flux

    Sodium-Free Refining Flux

    September 28, 2018Sodium-Free Refining FluxGeneral Description of Sodium-Free Refining Flux Aluminum alloys containing more than 2 % magnesium become brittle with sodium. Feature: This flux is a compact covering and cl...view
  • Granulated Fused Refining Fluxes

    Granulated Fused Refining Fluxes

    September 28, 2018General introduction: SATA granulated fused refining flux is a eutectic salt composed of mgcl2 anhydrous and potassium or sodium chloride. Which can removes alkali metal(sodium, calcium, lithium) and ...view
Leave a Message Email Us

we will contact you within 24 hours.